Material Type: NiCr A286
Material Group: Stainless Steel Wire
NiCr A286 Springs Description:
Cold drawn and precipitation hardened after fabrication. Good corrosion resistance at elevated temperatures. A Nickel-Chromium alloy with the addition of aluminum to give outstanding resistance to oxidation and other forms of high temperature corrosion with the ability to maintain high mechanical properties at elevated temperatures.
Available NiCr A286 Springs Material Forms
Wire: Yes Strip: Yes Sheet/Plate: Yes
Engineering Data
| E Mpa | 200,000 | Min Size (in) | 0.016 |
| E psi | 29,000,000 | Max Size (in) | 0.200 |
| G Mpa | 71,700 | Min Size (mm) | 0.400 |
| G psi | 10,400,000 | Max Size (in) | 5.000 |
| Density g/cm3 | 8.030 | Surface Min | b |
| Density lb/in3 | 0.290 | Max Temp °C | 510 |
| Conductivity | 2 | Max Temp °F | 950 |
All materials specifications are provided for general reference purposes only.
NiCr A286 Springs Notes:
| E Mpa | Young's Modulus | These factors can vary with cold work, heat treating and operational stress. | |
| E psi | |||
| G Mpa | Modulus of Rigidity | ||
| G psi | |||
| Conductivity | % IACS | ||
| Surface Min | Typical Surface Quality | a | Maximum defect depth: 0 to 0.5% of d or t |
| b | Maximum defect depth: 1.0% of d or t | ||
| c | Defect depth:less that 3.5% of d or t | ||
| Min Size | Sizes commonly available for wire or strip | Special sizes may be available at additional cost. | |
| Max Size | |||
| Max Temp | Maximum service temperature | May vary due to operating stress | |