Material Type: Beryllium Copper
Material Group: Copper Base Alloy Strip
Cold rolled and may be mill hardened before fabrication.. Good corrosion resistance and electrical conductivity. High physicals.
Available Beryllium Copper Springs Material Forms
Wire: No Strip: Yes Sheet/Plate: No
Engineering Data
| E Mpa | 128,000 | Min Size (in) | 0.003 |
| E psi | 18,000,000 | Max Size (in) | 0.375 |
| G Mpa | 48,300 | Min Size (mm) | 0.080 |
| G psi | 7,000,000 | Max Size (in) | 9.500 |
| Density g/cm3 | 8.260 | Surface Min | b |
| Density lb/in3 | 0.298 | Max Temp °C | 205 |
| Conductivity | 21 | Max Temp °F | 400 |
All materials specifications are provided for general reference purposes only.
| E Mpa | Young's Modulus | These factors can vary with cold work, heat treating and operational stress. | |
| E psi | |||
| G Mpa | Modulus of Rigidity | ||
| G psi | |||
| Conductivity | % IACS | ||
| Surface Min | Typical Surface Quality | a | Maximum defect depth: 0 to 0.5% of d or t |
| b | Maximum defect depth: 1.0% of d or t | ||
| c | Defect depth:less that 3.5% of d or t | ||
| Min Size | Sizes commonly available for wire or strip | Special sizes may be available at additional cost. | |
| Max Size | |||
| Max Temp | Maximum service temperature | May vary due to operating stress | |