 Material Type: NiCr A286
Material Group: Stainless Steel Wire
NiCr A286 Springs Description:
Cold drawn and precipitation hardened after fabrication. Good
corrosion resistance at elevated temperatures. A Nickel-Chromium alloy
with the addition of aluminum to give outstanding resistance to
oxidation and other forms of high temperature corrosion with the ability
to maintain high mechanical properties at elevated temperatures.
Available NiCr A286 Springs Material Forms
Wire: Yes Strip: Yes Sheet/Plate: Yes
Engineering Data
| E Mpa |
200,000 |
Min Size (in) |
0.016 |
| E psi |
29,000,000 |
Max Size (in) |
0.200 |
| G Mpa |
71,700 |
Min Size (mm) |
0.400 |
| G psi |
10,400,000 |
Max Size (in) |
5.000 |
| Density g/cm3 |
8.030 |
Surface Min |
b |
| Density lb/in3 |
0.290 |
Max Temp °C |
510 |
| Conductivity |
2 |
Max Temp °F |
950 |
All materials specifications are provided for general reference purposes only. |
NiCr A286 Springs Application:
|
| E Mpa |
Young's
Modulus |
These factors can vary with cold work, heat treating and operational
stress. |
| E psi |
| G Mpa |
Modulus of
Rigidity |
| G psi |
| Conductivity |
% IACS |
| Surface
Min |
Typical
Surface Quality |
a |
Maximum defect depth:
0 to 0.5% of d or t |
| b |
Maximum defect depth:
1.0% of d or t |
| c |
Defect depth:less that
3.5% of d or t |
| Min Size |
Sizes
commonly available for wire or strip |
Special sizes may be available at additional cost. |
| Max Size |
| Max Temp |
Maximum service
temperature |
May vary
due to operating stress |
NiCr A286 Springs